Tempered glass is also called safety glass, tempered after internal structure changes, hardness increased many times, toughened degree can reach differenthardness results, including 1mm, 2mm, 3mm more than half toughened glass,automobile, shockproof full toughened bulletproof glass etc.. In order to achievedifferent levels of hardness, the tempering process and machines are not the same. Toughened glass will explode, explode oneself rate is a normal phenomenon in 3%, but if the tempering procedure without debugging, temperedout the effect will be very poor, the explosive rate will increase. Then thetoughened glass factory in the production of what technology is of particular note.

1, the heating temperature: tempered glass is ordinary glass tempering furnaceafter high temperature is reached, control method, so the most important processis temperature, different thickness of glass required temperature is not the same,the thinner the thickness required temperature is higher, the unreasonabletemperature will lead to large glass, glass particles bending, surface roughnessetc..

2: heating time, heating time of the glass is also very important, glass heating time is generally a millimeter of between 40 to 50 seconds, Baidu per mm on the need to increase the 40-50 seconds, if the surface is punched, holes need to add a certain amount of time.